The ASTM A517 specification is the Standard Specification for Pressure Vessel Plates, Alloy Steel, High-Strength, Quenched and Tempered material used in the application of fusion welded boilers and pressure vessels. Under this specification, the plate thickness determines the grade selection and the mechanical properties. Plates 2.5" in thickness and under, will have minimum Yield Strength of 100 ksi. Plates over 2.5" in thickness will have a minimum Yield strength of 90 ksi. Typical applications include unfired vessels and tanks.
Supplementary Technology: HIC Test | NACE MR0175 | Z15 | Z25 | Z35 | S1 | S2 | S3 | S5 | S6 | S7 | S8 | S9 | S11 | S12 | S17.
Thickness: 6MM to 300MM,
Width: 1500mm to 4050mm,
Length: 3000mm to 15000mm
Gnee steel is specialized in supplying ASTM A517 steel plate. For more information of A517 steel plates, please check them in following:
ASTM A517 Grade A,A517 Gr.A,A517GrA steel plate
ASTM A517 standard specification for pressure vessel plates, alloy steel, high-strength, quenched and tempered.
The steel shall be killed and shall conform to the fine austenitic grain size requirement of Specification A20/A20M.
| A517 grade A Chemical Composition | |||||
| Grade | The Element Max (%) | ||||
| C | Si | Mn | P | S | |
| A517 grade A | 0.13-0.23 | 0.34-0.86 | 0.74-1.20 | 0.035 | 0.035 |
| Cr | Mo | B | Zr | ||
| 0.46-0.84 | 0.15-0.31 | 0.0025 | 0.04-0.16 | ||
Carbon Equivalent: Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%
| Grade | A517 grade A Mechanical Property | |||
| Thickness | Yield | Tensile | Elongation | |
| A517 grade A | mm | Min Mpa | Mpa | Min % |
| 6-65 | 690 | 795-930 | 16% | |
| 65-150 | 620 | 725-930 | 14% | |
ASTM A517 Grade B,A517 Gr.B,A517GrB steel plate
| A517 grade BChemical Composition | |||||
| Grade | The Element Max (%) | ||||
| C | Si | Mn | P | S | |
| A517 grade B | 0.13-0.23 | 0.13-0.37 | 0.64-1.10 | 0.035 | 0.035 |
| Cr | Mo | B | Ti | V | |
| 0.36-0.69 | 0.12-0.28 | 0.0005-0.005 | 0.01-0.05 | 0.02-0.09 | |
Carbon Equivalent: Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%
| Grade | A517 grade B Mechanical Property | |||
| Thickness | Yield | Tensile | Elongation | |
| A517 grade B | mm | Min Mpa | Mpa | Min % |
| 6-65 | 690 | 795-930 | 16% | |
| 65-150 | 620 | 725-930 | 14% | |
ASTM A517 Grade E,A517 Gr.E,A517GrE steel plate
| A517 grade EChemical Composition | |||||
| Grade | The Element Max (%) | ||||
| C | Si | Mn | P | S | |
| A517 grade E | 0.10-0.22 | 0.08-0.45 | 0.35-0.78 | 0.035 | 0.035 |
| Cr | Mo | B | Ti | V | |
| 1.34-2.06 | 0.36-0.64 | 0.001-0.005 | 0.005-0.11 | ||
Carbon Equivalent: Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%
| Grade | A517 grade E Mechanical Property | |||
| Thickness | Yield | Tensile | Elongation | |
| A517 grade E | mm | Min Mpa | Mpa | Min % |
| 6-65 | 690 | 795-930 | 16% | |
| 65-150 | 620 | 725-930 | 14% | |
ASTM A517 Grade F,A517 Gr.F,A517GrF steel plate
| A517 grade FChemical Composition | ||||||
| Grade | The Element Max (%) | |||||
| C | Si | Mn | P | S | Cu | |
| A517 grade F | 0.08-0.22 | 0.13-0.37 | 0.55-1.10 | 0.035 | 0.035 | 0.12-0.53 |
| Cr | Mo | B | V | Ni | ||
| 0.36-0.69 | 0.36-0.64 | 0.0005-0.006 | 0.02-0.09 | 0.67-1.03 | ||